FP3D™
Carbon, Inc. and Keystone Industries
Durable, translucent, dimensionally accurate, and flexible
-
Color / Shades
Original Pink, Light Reddish Pink, Dark Veined -
Flexural Modulus
800 MPa 116 ksi -
Flexural Strength
30 MPa 4 ksi -
Total Work Fracture
960 J/m2 -
ISO Standards
ISO 10993, ISO 20795-1
-
Ultimate Tensile Strength
33 MPa 5 ksi -
Tensile Modulus
1600 MPa 232 ksi -
Elongation At Break
7 % -
Impact Strength (Notched)
15 J/m 0.28 ft-lb/in -
Heat Deflection Temperature
40 °C 104 °F
-
Ultimate Tensile Strength
45 MPa 7 ksi -
Tensile Modulus
1800 MPa 261 ksi -
Elongation At Break
4 % -
Impact Strength (Notched)
20 J/m 0.37 ft-lb/in -
Heat Deflection Temperature
60 °C 140 °F
-
Color / Shades
Bleach, A1, A2, B1 -
ISO Standards
FDA Exempt Class II -
Wear Rate (wt)
< 0.8 mm3 -
Coffee Staining
2.41 ΔE / 28 days
-
Color / Shades
Original Pink, Opaque Original Pink, Dark Reddish Pink, Light Pink -
Wear Rate (wt)
0.0686 mm3 / 10 years -
Total Work Fracture
1209 J/m2 -
Fracture Toughness
2.82 MPa · m½
-
Color
A1, A2, B1, Bleach, and Hollywood White -
Total Work Fracture
1033 J/m2 -
Fracture Toughness
2.9 MPa · m½ -
Flexural Strength
126 MPa 18 ksi -
Flexural Modulus
4281 MPa 621 ksi
Lucitone Digital Print™
Dentsply Sirona
High impact fracture resistance, color stable, highly accurate
-
Flexural Strength
>65 MPa >9 ksi -
Work Fracture
>900 MPa >131 ksi -
Flexural Modulus
>2000 MPa >290 ksi -
Impact Strength (Notched)
Exceeds ISO high impact standards
Lucitone Digital IPN™ 3D Premium Tooth
Dentsply Sirona
Versatile, durable, premium
-
Shades
16 A-D shades and 2 Bleach Shades -
Wear Resistance
Superior Durability of Traditional IPN®️ -
Flexural Strength
135 MPa 20 ksi -
Flexural Modulus
2900 MPa 421 ksi -
Compressive Strength
142 MPa 21 ksi -
ISO Standards
ISO 10477
Lucitone Digital Value™ 3D Economy Tooth and Trial Placement
Dentsply Sirona
Versatile, durable, economical
-
Flexural Strength
>65 MPa >9 ksi -
Work Fracture
>900 MPa >131 ksi -
Flexural Modulus
>2000 MPa >290 ksi -
ISO Standards
ISO 22112
Flexcera™ Smile Ultra+
Desktop Health™
Extraordinary strength, beauty, and functionality
-
Shades
Bleach, A1, A2, B1 -
Water Absorption
1.96 wt% -
Volumetric Wear
0.012 mm3 -
Total Work Fracture
1301 ±287.5 J/m2
-
Flexural Modulus
2322 +/- 114 MPa 0-17 ksi -
Sorption
31.9 +/- 0.6 μg/mm3 -
Shades
Light Pink, Original Pink, Medium Pink, Dark Pink, Dark Meharry -
Solubility
0.1 +/- 0.2 μg/mm3
-
Flexural Modulus
>2000 MPa >290 ksi -
Flexural Strength
>65 MPa >9 ksi -
ISO Standards
ISO 20795 -
Shades
Bleach, A1, A2, A3, A3.5, B1
-
Flexural Modulus
>2000 MPa >290 ksi -
Flexural Strength
>65 MPa >9 ksi -
ISO Standards
ISO 20795 -
Shades
Light Pink, Original Pink, Medium Pink, Dark Pink, Dark Meharry
-
Color
Clear -
Flexural Modulus
1107 MPa 161 ksi -
Flexural Strength
37 MPa 5 ksi -
Durometer (Shore A Hardness)
76 A
-
Durometer (Shore A Hardness)
75-90 A -
Tear Strength
30 kN/m 171.3 lbf/in -
Color
White, black, green, and purple
-
Ultimate Tensile Strength
2 MPa 0 ksi -
Tensile Modulus
4.6 MPa 1 ksi -
Elongation At Break
41 % -
Color
Pink
-
Color
Tinted -
Flexural Modulus
2400 MPa 348 ksi -
Flexural Strength
106 MPa 15 ksi -
Biocompatibility
ISO 10993-5 and ISO 10993-10
-
Color
Clear and Tinted -
Flexural Modulus
2300-2400 MPa 334-348 ksi -
Flexural Strength
100-110 MPa 15-16 ksi -
Biocompatibility
ISO 10993 -
Impact Strength (Notched)
29 J/m 0.54 ft-lb/in
-
Color
Clear -
Flexural Modulus
1000 MPa 145 ksi -
Flexural Strength
38 MPa 6 ksi -
Biocompatibility
ISO 10993 -
Impact Strength (Notched)
45-48 J/m 0.84-0.9 ft-lb/in
KeyDenture Try-In™
Keystone Industries®
Excellent surface finish, fast and cost-effective
-
Shades
A1, B1, BL4 -
Flexural Modulus
1500-1750 MPa 218-254 ksi -
Flexural Strength
56-68 MPa 8-10 ksi -
Biocompatibility
ISO 10993
-
Color / Shades
0M1, 0M3, B1, A1, A2, A3 -
Total Work Fracture
2442 ± 296 J/m2 -
Flexural Strength
141 - 170 MPa 20-25 ksi -
Flexural Modulus
3800 - 4700 MPa 551-682 ksi
-
Flexural Modulus
2900 MPa 421 ksi -
Flexural Strength
84 MPa 12 ksi -
Biocompatibility
ISO 10993-1
-
Shades
BL, B1, A1, A2, A3, C2 -
Flexural Modulus
6500 MPa 943 ksi -
Wear Rate (wt)
1.4 mg/million cycles -
Fracture Toughness
1.4 Klc -
Radiodensity
Radio-opaque -
Water Absorption
14.5 µg/mm3/td
-
Color / Shades
Pink, Pink Translucent -
Durometer (Shore D Hardness)
>75 D -
Flexural Modulus
>2000 MPa 0 ksi -
Flexural Strength
>65 MPa 0 ksi -
Fracture work
14 - 25 kJ/m ² -
Water Absorption
< 32 μg/mm³ -
Water solubility
< 1.6 μg/mm³
-
Color / Shades
0M3, A1, A2, A3, A3.5, B1, B3, C2, D3 -
Durometer (Shore D Hardness)
≥ 80 D -
Flexural Modulus
2800 MPa 406 ksi -
Flexural Strength
>100 MPa 0 ksi -
Water Absorption
<40 ug/mm³ -
Water solubility
< 7.5 μg/mm³
-
Color / Shades
Tooth-colored resin (≈A2) -
Durometer (Shore D Hardness)
≥ 75 D -
Flexural Modulus
2200 MPa 319 ksi -
Flexural Strength
>100 MPa 0 ksi -
Water Absorption
< 40 μg/mm³ -
Water solubility
< 7.5 μg/mm³
Crown and Bridge Resin
Dentca
Accurate, color-matched, FDA cleared class II device
-
Elongation At Break
7.5 % -
Flexural Modulus
2000 MPa 290 ksi -
Flexural Strength
100 MPa 15 ksi -
Cauterization Residual Ash Content
1.5 %
-
Hardness (Room)
90 Shore A -
Hardness (Body)
80 Shore A -
Elongation At Break
45 % -
Printed Accuracy
50 μm
-
Flexural Modulus
>2100 MPa >305 ksi -
Flexural Strength
>90 MPa >13 ksi -
Color
Green Transparent
-
Tensile Modulus
1700 MPa 247 ksi -
Flexural Strength
90 MPa 13 ksi -
Elongation At Break
10 % -
Hardness
80 Shore D